17-4ph hmoov Metallurgy Pressed Parts

Khoom Taw Qhia

Txheej txheem ntau lawm

Hom 17-4PH yog martensitic nag lossis daus-hardening stainless hlau muab kev sib xyaw zoo heev ntawm lub zog siab, zoo corrosion kuj, zoo mechanical zog ntawm qhov kub txog li 600 degree F (316 degree), zoo toughness nyob rau hauv ob lub hauv paus hlau thiab welds , thiab luv luv, kev kho cua sov qis kom txo qis warping thiab scaling.

Stainless hlau 134-Nickel-based alloy 7278-Hastelloy 7990 Legends Sau tag nrho cov lej saum toj no los hu rau Moju Special Steel cov neeg siv khoom.

Tshuaj muaj pes tsawg leeg ntawm 17-4PH stainless hlau

Cov pa roj carbon: siab tshaj {{0}}.{{20}}70 manganese: siab tshaj 1.00 silicon: siab tshaj 1.00 chromium : 15.00-17.00 npib tsib xee: 3. ntxiv rau 钽: yam tsawg kawg 5 carbon -0.45 siab tshaj phosphorus: 0.040 Maximum sulfur: 0.030 Maximum hlau: sib npaug 17-4PH execution standard AMS 5523, AST MA16717-4PH Lub cev ua haujlwm ntawm stainless hlau? Qhov ceev: 0.28 lbs/in3 7.80 g/cm317-4PH Resistivity: (microhm-cm): 68 degree F (20 degree): 98 Kub Kub: BTU/lbl degree F (kJ/ kg K): 32-212 degree F ({35}} degree): 0.11 (0.46) 17-4PH Thermal conductivity: BTU/hr/ft2/ ft/ degree F (W/mK) ntawm 300 degree F (149 degree): 124 (17.9) ntawm 900 degree F (482 degree): 157 (22.6) 17-4PH Nruab Nrab Coefficient ntawm Thermal Expansion: 70-200 degree F (21-93 degree ): 6.0 x 10-5 (10.8) 70-600 degree F (21-315 degree): 6.2 x 1 o-6 (11.2) 70-800 degree F ({{ 69}} degree): 6.3 x 10-5 (11.3) 17-4PH Modulus ntawm elasticity: 200 x 10311 hauv nro 78 x 10317-4PH hauv torsion Sib nqus permeability: Muaj zog ferromagnetic nyob rau hauv txhua rooj plaub { {80}}PH Mechanical zog 17-4PH Stainless hlau khoom nyob rau hauv lub annealed mob ASTM A69 3AMS 5604AM 5604

Qhov kawg Tensile Strength: Max. 1255 MPa Max. Yield Strength (0.2 feem pua ​​Offset): Max. 1105 MPa Elongation: 3% Min. Hardness: Max. 38 Re Heat Treatment Ability (Aging) H900 Qhov kawg Tensile Strength: 1310 MPa min. Tawm Zog: 1170 MPa Min. 25 Qhov kawg Tensile Strength: 1070 MPa Yield Strength: 1000 MPa Elongation: 5 feem pua ​​min Hardness: H1075 Qhov kawg Tensile Strength: 1000 MPa min Yield Strength: 860 MPa min Elongation: 5 feem pua ​​​​ntawm Tensile Strength: H110 min MPa min Yield Strength: 790 MPa min Elongation: 5% min Hardness: H1150 Qhov kawg Tensile Strength: 930 MPa Yield Uniform Strength: 725 MPa Elongation: 8 feem pua ​​min Hardness: H1400 plus 1150 Ultimate Tensile Strength: 930 MPa Strength: : 9%. 17-4PH Surface Treatment #1 - Kub dov annealed thiab descaled. Nws tuaj nyob rau hauv strips, foils, thiab ribbons. Nws yog siv nyob rau hauv daim ntawv thov uas tsis xav tau ib tug du tiav. #2D - Matt tiav ua los ntawm txias dov, annealing, thiab descaling. Rau qhov sib sib zog nqus kos thiab qhov chaw uas yuav tsum tau khaws cov roj nplua nyeem thaum lub sij hawm tsim. #2B - Smooth nto ua los ntawm txias dov, annealing, thiab descaling. Tom qab annealing, me ntsis txias dov dhau siv polished yob muab nws ib tug finer nto tiav tshaj 2D. #BA - Bright annealed txias dov thiab ci annealed #CBA - ci annealed txias dov matte tiav thiab ci annealed #2 - txias dov #2BA - du nto ua los ntawm txias dov thiab ci annealed. Ib lub teeb hla nrog cov menyuam polished heev ua rau ua kom tiav. 2BA topcoats tuaj yeem siv rau kev siv lub teeb molding uas yuav tsum tau ua kom tiav glossy ntawm molded qhov chaw. Polishing - Ntau yam grits rau cov kev xav tau polishing. 17-4ph hmoov metallurgy pressed qhov chaw alloy hlau nto XC - ntxiv huv si ci annealed los yog ci ntsa iab annealed thiab txias dov roj - ntxiv ci tiav (rau cov ntaub ntawv kho kom zoo nkauj) 17-4PH kev kho cua sov 17-4PH hom tuaj yeem kho cua sov los txhim kho cov khoom siv kho tshuab. 17-4PH Application Areas Surgical Sites Aerospace Chemicals Petrochemical Food Processing

Hlau Txhaj Moulding txheej txheem

Detection Systems